Raschig Group DECAL® 2061 Phenolic

Category Polymer , Thermoset , Phenolic
Manufacturer Raschig Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group DECAL® 2061 Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)Processing: Injection and Transfer moldingInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.30 - 1.40 g/cc
1.30 - 1.40 g/cc
ISO 1183
Apparent Bulk Density 0.500 - 0.700 g/cc
0.0181 - 0.0253 lb/in³
ISO 60
Water Absorption <= 1.20 %

@Temperature 23.0 °C,
Time 86400 sec
<= 1.20 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00900 - 0.0110 cm/cm
0.00900 - 0.0110 in/in
Injection; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Modulus of Elasticity 4.00 - 6.00 GPa
580 - 870 ksi
Injection; ISO 527
Flexural Strength 90.0 - 110 MPa
13100 - 16000 psi
Injection; ISO 178
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection; ISO 178
Compressive Strength 200 - 250 MPa
29000 - 36300 psi
ISO 604
Charpy Impact Unnotched 0.600 - 0.900 J/cm²
2.86 - 4.28 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.200 - 0.400 J/cm²
0.952 - 1.90 ft-lb/in²
Injection; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 - 40.0 µm/m-°C

@Temperature 50.0 - 150 °C
19.4 - 22.2 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Thermal Conductivity 0.200 - 0.400 W/m-K
1.39 - 2.78 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) 160 - 180 °C
320 - 356 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Shrinkage 0.500 - 0.700 %

@Temperature 110 °C,
Time 605000 sec
0.500 - 0.700 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 - 1.00e+17 ohm-cm
1.00e+16 - 1.00e+17 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 - 1.00e+14 ohm
1.00e+13 - 1.00e+14 ohm
IEC 60093
Dielectric Constant 4.00 - 6.00

@Frequency 1.00e+6 Hz
4.00 - 6.00

@Frequency 1.00e+6 Hz
IEC 60250
12.0 - 16.0

@Frequency 100 Hz
12.0 - 16.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
IEC 60243-1
Dissipation Factor 0.0600 - 0.0800

@Frequency 1.00e+6 Hz
0.0600 - 0.0800

@Frequency 1.00e+6 Hz
IEC 60250
0.600 - 0.800

@Frequency 100 Hz
0.600 - 0.800

@Frequency 100 Hz
IEC 60250
Arc Resistance 60.0 - 120 sec
60.0 - 120 sec
ASTM D495
Comparative Tracking Index >= 150 V
>= 150 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 20.0 - 30.0 °C
6.00 Month

@Temperature 68.0 - 86.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 900/1
IEC 60695 2-12
Glow wire ignitability test 900/1
IEC 60695 2-13
Water Absorption <60 mg
24 hr, 23°C; ISO 62