Polyram RamSter PF306G6 PBT, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF306G6 PBT, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber reinforced, low viscosity PBT for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 9.90 GPa | 1440 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.20 kJ/m² @Temperature -30.0 °C |
4.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.870 J/cm² @Temperature -30.0 °C |
4.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 30 mm/min | 1.2 in/min | FMVSS302 |
| Glow Wire Test | 650 °C | 1200 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Techmer ES Plastiblend® POM CO UV BK
- Borealis BF335SA Polypropylene Copolymer
- Plastics Group Polifil® GFPPCC-30 30% Glass Reinforced Polypropylene
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- ELM® SoyEasy™ OGL Biodegradable – Biobased Open Gear Lubricant
- Colorite Polymers 9011 Clear Extrusion Vinyl Compound
- 3M Scotchcal™ 3632-015 Translucent Film
- 3M 5850 Clean-View Pad
- Radici Heraflex® A 35-13-40 TPS-SEBS Thermoplastic Elastomer
- Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved