ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 204°C Temper

Category Metal , Ferrous Metal , Stainless Steel , T 400 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 204°C Temper.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steels. Oil quenching this alloy from temperatures between 1800°F and 1950°F produces the high strength and/or wear resistance as well as corrosion resistance.A major use for this grade of heat treatable stainless steel is in cutlery. When blanking cutlery parts from annealed raw material stock, Type 425 Mod will usually exhibit hardness, yield strength, and tensile strength that are low enough for fine blanking purposes.UTS, TYS, and hardness values below obtained after austenitizing at 1800-1950°F (982-1066°C) followed by an oil quench and two hour temper as above.Information provided by Allegheny Ludlum Corporation.
Physical Properties Metric English Comments
Density 7.72 g/cc
0.279 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 53
53
Tensile Strength, Ultimate 1868 MPa
270900 psi
Typical
Tensile Strength, Yield 1385 MPa

@Strain 0.200 %
200900 psi

@Strain 0.200 %
typical
Modulus of Elasticity 200 GPa
29000 ksi
Thermal Properties Metric English Comments
CTE, linear 11.6 µm/m-°C

@Temperature 20.0 - 200 °C
6.44 µin/in-°F

@Temperature 68.0 - 392 °F
12.8 µm/m-°C

@Temperature 20.0 - 600 °C
7.11 µin/in-°F

@Temperature 68.0 - 1110 °F
Thermal Conductivity 24.207 W/m-K

@Temperature 100 °C
168.00 BTU-in/hr-ft²-°F

@Temperature 212 °F
Melting Point 1472 - 1510 °C
2682 - 2750 °F
Solidus 1472 °C
2682 °F
Liquidus 1510 °C
2750 °F
Component Elements Properties Metric English Comments
Carbon, C 0.50 - 0.55 %
0.50 - 0.55 %
Chromium, Cr 13 - 14 %
13 - 14 %
Iron, Fe 85 %
85 %
as balance
Manganese, Mn <= 1.0 %
<= 1.0 %
Molybdenum, Mo 0.80 - 1.2 %
0.80 - 1.2 %
Nickel, Ni <= 0.50 %
<= 0.50 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S <= 0.030 %
<= 0.030 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000610 ohm-cm
0.0000610 ohm-cm