- Polyram RamSter PF302G3 PBT, 15% Glass Fiber, UV Stabilized
Polyram RamSter PF302G3 PBT, 15% Glass Fiber, UV Stabilized
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PF302G3 PBT, 15% Glass Fiber, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass fiber reinforced, UV stabilized PBT for injection molding application.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ISO 2577 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 250 °C |
17 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 4.40 GPa | 638 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 650 °C | 1200 °F | GWIT; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Fiberfil® PP-60/TC/10 Polypropylene Homopolymer, 10% Talc Filled
- Gromax BFM30-EL04B2 Nylon 6 30% Mineral Filled (Dry)
- Solvay Chemicals NOCOLOK® Flux Drystatic Potassium Fluoroaluminate
- Cytec Thornel® Mat VMD Carbon Fiber
- DuPont Performance Polymers Delrin® FG511DP NC010 Acetal (POM) (Unverified Data**)
- Clariant Renol PA2SP0017 Nylon 6, Impact Modified
- 3M 25X187 Protective UV Tape
- 3M 4000 UV 6586 Marine Adhesive/Sealant Fast Cure
- 3M 8420-6 Cold Shrink Connector Insulators