- Polyram RamOfin PPC361T4 Polypropylene, 20% Mineral Filled
Polyram RamOfin PPC361T4 Polypropylene, 20% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPC361T4 Polypropylene, 20% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Mineral filled, heat resistant polypropylene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ISO 2577 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 120 °C | 248 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- MV Labs PD250 Na2PdBr4 Sodium tetrabromopalladate(II)
- LG Chemical LUPOS HR-2207 Heat Resistant SAN, 20% Glass Fiber Reinforced
- Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb
- Hexcel® HexWeb® CR-PAA™ 5/32-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb
- A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound
- DuPont Performance Polymers VESPEL TP-8474 Polyimide
- 3M Scotchcal™ 50-1 Graphic Film
- E-Polymers SEPAZ® LB40 PA6 LFT Resin
- Unipetrol PE HD LITEN® MB/ML 57 HDPE
- Eurostar Star L PA66 15Y D52 PA66, Carbon Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved