NIZHNEKAMSKNEFTEKHIM PE 4148B (484H2) High Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 4148B (484H2) High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 - 0.950 g/cc | 0.0342 - 0.0343 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 0.15 - 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 - 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 3.0 - 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
3.0 - 6.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 20; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 52.0 MPa | >= 7540 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 48.0 MPa | >= 6960 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 480 % | >= 480 % | ASTM D882 |
| Film Elongation at Break, TD | >= 600 % | >= 600 % | ASTM D882 |
| Tensile Modulus | >= 0.650 GPa | >= 94.3 ksi | 2% sec, TD; ASTM D882 |
| >= 0.700 GPa | >= 102 ksi | 2% sec, MD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 0.512 g/micron | >= 13.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 2.36 g/micron | >= 60.0 g/mil | ASTM D1922 |
| Dart Drop Test | >= 170 g | >= 0.375 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 600 |
Users viewing this material also viewed the following:
- MV Labs CR890 (NH4)2Cr2O7 Ammonium dichromate
- Plastcom SLOVAMID 6 GF 25 FRC 3 PA6, 25% glass fibre, flame retardant
- Polymer Resources ABS-GP-IM General Purpose ABS, Impact Modified
- Teknor Apex MF 09-G0288A-87NT Polyvinyl Chloride, Flexible Film
- Solvay TECHNYL® A 205F PA66, Conditioned
- Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide
- Plastics Group Polifil® 836L Nylon 6 (DAM)
- Daikin DAI-EL G-783 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- DuPont Performance Polymers Crastin® SK692FR NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- Adell BJ-14 Nylon 6, 20% Glass Reinforced; High Impact
Copyright © lookpolymers.com All Rights Reserved