ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Hot Rolled Steel

Category Metal , Ferrous Metal , Alloy Steel
Manufacturer ArcelorMittal
Trade Name Complex Phase Steel
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Hot Rolled Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Available in the following: Extragal®/Galvannealed (HCT950C+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A number of automotive parts, such as sills and door reinforcements, have simple shapes and the steel is therefore only slightly deformed. For this reason, ArcelorMittal has added the Complex Phase family of steels to its range. These steels offer high as-delivered yield strength and good bendability and stretch flangeability.Applications: Given their high energy absorption capacity and fatigue strength, these grades are particularly well suited for automotive safety components requiring good impact strength and for suspension system components.Information provided by ArcelorMittal
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate >= 950 MPa
>= 138000 psi
Tensile Strength, Yield 800 - 950 MPa
116000 - 138000 psi
Elongation at Break >= 10 %
>= 10 %
L<Sub>0</sub>=80 mm, th<3 mm
Fatigue Strength <= 660 MPa

@# of Cycles 2.00e+6
<= 95700 psi

@# of Cycles 2.00e+6
<= 660 MPa

@# of Cycles 1.00e+7
<= 95700 psi

@# of Cycles 1.00e+7
<= 750 MPa

@# of Cycles 100000
<= 109000 psi

@# of Cycles 100000
Component Elements Properties Metric English Comments
Carbon, C <= 0.14 %
<= 0.14 %
Iron, Fe >= 97.91 %
>= 97.91 %
as balance
Manganese, Mn <= 1.7 %
<= 1.7 %
Silicon, Si <= 0.25 %
<= 0.25 %