Bhansali Engineering Abstron IM-17A(HF) ABS Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bhansali Engineering Abstron IM-17A(HF) ABS Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very High Flow, Medium Impact GradeInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.045 g/cc | 0.03775 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 62 g/10 min @Load 10.0 kg, Temperature 220 °C |
62 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D-785 |
| Tensile Strength, Yield | 41.7 MPa @Thickness 3.20 mm |
6040 psi @Thickness 0.126 in |
Type 1; ASTM D-638 |
| Flexural Yield Strength | 60.8 MPa @Thickness 6.40 mm |
8820 psi @Thickness 0.252 in |
ASTM D-790 |
| Flexural Modulus | 2.16 GPa @Thickness 6.40 mm |
313 ksi @Thickness 0.252 in |
ASTM D-790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.40 mm |
2.76 ft-lb/in @Thickness 0.252 in |
ASTM D-256 |
| 1.7647 J/cm @Thickness 3.20 mm |
3.3060 ft-lb/in @Thickness 0.126 in |
ASTM D-256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Vicat Softening Point | 102 °C | 216 °F | Method B; ASTM D-1525 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
UL-94 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GB 30 PBT, 30% glass beads
- LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (Unverified Data**)
- Silberline SilBerCote® 553-20Y
- Saint-Gobain Norton® V770 Low-Density Pressure Sensitive Adhesive Sealant Foam
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Eagle Brass 715 Copper Nickel 30%, Annealed
- Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- Arkema Group Rilsan® BZM 43 G9 Nylon 11, 43% Glass Fiber Filled (Dry)
- BASF Neopolen® P 9035 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- Covestro Makrolon® Rx1851 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved