- Polyram PlusTek RA303G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
Polyram PlusTek RA303G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA303G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% Glass fiber reinforced, heat stabilized and hydrolysis resistant Nylon 66 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.0 % | 4.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | |
| Tensile Strength, Yield | 215 MPa | 31200 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 300 MPa | 43500 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous use |
| 230 °C | 446 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Karina E818-18/99-CRM Gray PVC Compound
- Solvay Sulfuric Acid 98% Water White Grade
- ExxonMobil Spartan EP 150
- DSM Arnitel® EL550 Polyether Ester Elastomer (European and Asian Grade)
- Advanced Polymer Alloys DuraGrip™ DGR 6140 UT Thermoplastic Elastomer (TPE)
- Addiplast Addilene J 683 Polypropylene Copolymer
- E-Polymers EFLEX® V1070 EPDM/TPV
- Braskem HF 0147 HDPE Blown Film Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved