Polyram PlusTek PB702 Nylon 6, UV Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB702 Nylon 6, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 6 UV stabilized for fast cycle injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Water Absorption | 9.5 % | 9.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.012 - 0.016 cm/cm | 0.012 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM-D785 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM-D638 |
| Elongation at Break | 15 % | 15 % | ASTM-D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 100 kV/mm | 2540 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 945A PC (Europe-Africa-Middle East)
- Sylvin Technologies 9925-65 Natural PVC Molding Compound
- SABIC Innovative Plastics LNP Thermotuf R1000IX2 PA6.6 (Europe-Africa-Middle East)
- Struktol VP 3752 Flame retarded epoxy resin
- UBE UBESTA® 3014U Rigid Electronic Grade Nylon 12
- Hexcel® HexForce™ 6781HT Fiber Glass Fabric
- Goodfellow Vanadium 75/Chromium 25 Alloy
- Fainplast Compounds Hax™ HFX 505 Crosslinkable HFFR Cable Compound
- Premix Premi-Glas® 1200-28 Polyester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved