Polyram PlusTek PA862 Nylon 6.6 for Injection Molding, High Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA862 Nylon 6.6 for Injection Molding, High Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.7 % | 6.7 % | ISO 62 |
| Linear Mold Shrinkage | 0.017 - 0.025 cm/cm | 0.017 - 0.025 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 50 % | 50 % | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Continuous use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 12.2 mm/min | 0.480 in/min | FMVSS302 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- IRPC Polimaxx Polene 2500H Polypropylene Block Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66
- Vyncolit X658 Novolac Phenolic
- A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene
- American Elements Cobalt Oxide Nanopowder
- ExxonMobil Escorene™ UL 15028CC Ethylene Vinyl Acetate Copolymer (European Grade)
- ExxonMobil 220 Mobil SHC PM Series
- Bhansali Engineering Abstron IM-17A ABS Injection Molding Grade
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A
- Kazanorgsintez P2ES-12 Electrically Conductive Polyethylene Composite
Copyright © lookpolymers.com All Rights Reserved