Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Interleave: 1.5 mil PolyethyleneSide 1: Cured Silicone RubberSubstrate: Style 2116 FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 |
| 102 microns | 4.00 mil | Substrate; Arlon SQA-TMS-003 | |
| 152 microns | 6.00 mil | Overall Thickness; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 |
| Tensile Strength | 5.72 MPa | 830 psi | Silicone Property; ASTM D412 |
| Elongation at Break | 150 % | 150 % | Silicone Property; ASTM D412 |
| Tear Strength | 9.64 kN/m | 55.0 pli | Silicone Property; Die B; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability Test | 0.25 | 0.25 | Inches; Char Length; FAR 25.853 App F, Pt. 1, S. Aii |
| 1.0 | 1.0 | Seconds; Flame and Glow Time; FAR 25.853 App F, Pt. 1, S. Aii |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 59.1 kV/mm | 1500 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| Shelf Life | 60.0 Month @Temperature 23.9 °C |
60.0 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 5.6 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- Nyco NYGLOS® M3 Wollastonite
- Nye Lubricants 300 (SO) Synthetic Oil
- PTS Trimid® N6-200N Nylon 6 with Nucleating Agent
- Petroquimica Triunfo Trilene® TS 8058 LLDPE-C6 and LDPE Blend
- Kazanorgsintez 298-285 High Density Polyethylene Composite
- Ultracor® UCF-355-3/8-3.5 Honeycomb Core Material
- Ultracor® UCF-51-3/8-2.0 Honeycomb Core Material
- Arlon 56106R026 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Momentive Performance Materials HCV Boron Nitride (BN) Powder
- KKPC KOSYN KTR 601 Thermoplastic Elastomer (TPE)
Copyright © lookpolymers.com All Rights Reserved