Polymer Resources TP-GP1-IM Polybutylene Terephthalate, Impact Modified, Medium Flow
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Impact Grade |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources TP-GP1-IM Polybutylene Terephthalate, Impact Modified, Medium Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polybutylene Terephthalate, Impact Modified, Medium FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | ASTM D955 |
| Melt Flow | 10 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 - 20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.9 MPa | 6800 psi | ASTM D638 |
| Tensile Strength, Yield | 46.9 MPa | 6800 psi | ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 249 °C | 450 - 480 °F | |
| Middle Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 43.3 - 76.7 °C | 110 - 170 °F | |
| Drying Temperature | 116 - 121 °C | 240 - 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PK-30GF/000 Polyetheretherketone (PEEK)
- KaMin Polyplate® HMT Kaolin Clay - Delaminated
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
- Techmer ES HiFill® PA4/6 GF33 HS NAT 33% Glass Filled (Conditioned)
- Zylog Hipolyene® 2703 MS Thermoplastic Polyolefin & PP Compound
- Denka REOMER G G8354 Thermoplastic Elastomer, For Injection Molding
- Aptek DI-STRATE 95217 Microwave/RF Foam Substrate
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- Axiall 8791 Moldings & Extrusions Flexible PVC
- SABIC Innovative Plastics NORYL GTX CRN730V PPE+PA6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved