Polymer Resources PPX-SF1 Modified-PPO, Structural Foam Grade, Flame Retardant, Easy Flow

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX-SF1 Modified-PPO, Structural Foam Grade, Flame Retardant, Easy Flow.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Modified-Polyphenylene Oxide, Structural Foam Grade, Easy FlowFeatures: • Flame Retardant • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.12 g/cc	1.12 g/cc	ASTM D792
Linear Mold Shrinkage	0.0060 - 0.0090 cm/cm	0.0060 - 0.0090 in/in	ASTM D955
Melt Flow	25 - 50 g/10 min @Load 11.6 kg, Temperature 250 °C	25 - 50 g/10 min @Load 25.6 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM D785
Tensile Strength at Break	62.1 MPa	9000 psi	ASTM D638
Tensile Strength, Yield	63.4 MPa	9200 psi	ASTM D638
Flexural Strength	82.7 MPa	12000 psi	ASTM D790
Flexural Modulus	3.17 GPa	460 ksi	ASTM D790
Izod Impact, Notched	1.07 J/cm @Temperature 22.8 °C	2.00 ft-lb/in @Temperature 73.0 °F	ASTM D256
Gardner Impact	16.9 J	12.5 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	104 °C	220 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	98.9 °C	210 °F	ASTM D648
UL RTI, Electrical	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
	65.0 °C @Thickness 3.81 mm	149 °F @Thickness 0.150 in	UL 746
UL RTI, Mechanical with Impact	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
	65.0 °C @Thickness 3.81 mm	149 °F @Thickness 0.150 in	UL 746
UL RTI, Mechanical without Impact	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
	65.0 °C @Thickness 3.81 mm	149 °F @Thickness 0.150 in	UL 746
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in
	V-0 - 5VA @Thickness 3.80 mm	V-0 - 5VA @Thickness 0.150 in

Processing Properties	Metric	English
Rear Barrel Temperature	232 - 260 °C	450 - 500 °F
Middle Barrel Temperature	271 - 304 °C	520 - 580 °F
Front Barrel Temperature	271 - 304 °C	520 - 580 °F
Melt Temperature	260 - 288 °C	500 - 550 °F
Mold Temperature	37.8 - 82.2 °C	100 - 180 °F
Drying Temperature	71.1 - 82.2 °C	160 - 180 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour