SABIC Innovative Plastics NORYL EXNL0303 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL EXNL0303 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EXNL0303 is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. Noryl EXNL0303 is available in custom colors and may be an excellent material candidate for applications requiring light weight parts and may be processed by injection molding or extrusion techniques.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.27 % | 0.27 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18.3 g/10 min @Load 5.00 kg, Temperature 280 °C |
18.3 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| 42.7 g/10 min @Load 5.00 kg, Temperature 300 °C |
42.7 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 280 °C |
17 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 41 g/10 min @Load 5.00 kg, Temperature 300 °C |
41 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | ISO 527 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 27.5 % | 27.5 % | Type I, 50 mm/min; ASTM D638 |
| 27.8 % | 27.8 % | ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| 4.2 % | 4.2 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.43 GPa | 352 ksi | 1 mm/min; ISO 527 |
| 2.45 GPa | 355 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.38 GPa | 345 ksi | ISO 178 |
| 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ASTM D256 |
| 1.17 J/cm @Temperature -30.0 °C |
2.19 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*3; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 83.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 85.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 127 °C | 261 °F | Rate B/50; ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Draeger Tube Toxicity, Flaming (1.52mm) | Pass | AITM 3.0005, ABD0031 |
| Draeger Tube Toxicity, Non-Flaming (1.52mm) | Pass | AITM 3.0005, ABD0031 |
| NBS Smoke Density, Flaming, 20 min (3.2 mm) | 126 | ASTM E 662 |
| NBS Smoke Density, Flaming, 4 min (1.52mm) | 29 | ASTM E 662 |
| NBS Smoke Density, Flaming, 4 min (3.2 mm) | 35 | ASTM E 662 |
| NBS Smoke Density, Non-Flaming, 4 min (1.52mm) | 7 | ASTM E 662 |
| Vertical Burn a (60s, 1.52mm) passes at | 0sec | FAR 25.853 |
| Vertical Burn b (12s, 1.52mm) passes at | 4sec | FAR 25.853 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 180 (2400 Viscosity) Rapid Bonding Adhesive
- Nanocyl EPOCYL™ NC E1MY-02 Master Batch Liquid tetrafunctional epoxy Resin for non-Solvent Formulation Purposes
- Styron CALIBREâ„¢ 320 UV Polycarbonate Resin
- Hexcel® HexWeb® HRH-36® Flex-Core® HRH-36 - F50 - 3.0 Aramid Honeycomb
- Ter Hell Plastic Terez® PA 6.6 HT 7110 GF 41 FL-HF/2 Polyamide 66 Copolymer, 41% Glass Fiber
- EMS-Griltech Grilon® XC 130 Nylon 610 Monofilament (Non-Set)
- Chi Mei Polylac® PA-764B ABS - Flame Retardant
- Akzo Nobel Expancel® 551 DE 80 d42 Dry expanded microspheres
- Indium Corp. Indalloy 190 Aluminum Solder Alloy
Copyright © lookpolymers.com All Rights Reserved