Polymer Resources PPX-FR2 Modified-PPO, V-1 Flame Retardant

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-FR2 Modified-PPO, V-1 Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 20 - 40 g/10 min

@Load 11.6 kg,
Temperature 250 °C
20 - 40 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7100 psi
ASTM D638
Tensile Strength, Yield 50.3 MPa
7300 psi
ASTM D638
Elongation at Break 25 %
25 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm

@Temperature -30.0 °C
2.00 ft-lb/in

@Temperature -22.0 °F
ASTM D256
2.67 J/cm

@Temperature 22.8 °C
5.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Charpy Impact, Notched 1.68 J/cm²

@Temperature 22.8 °C
8.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 98.9 °C
210 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.3 °C
200 °F
ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
65.0 °C

@Thickness 5.99 mm
149 °F

@Thickness 0.236 in
UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
65.0 °C

@Thickness 5.99 mm
149 °F

@Thickness 0.236 in
UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
65.0 °C

@Thickness 5.99 mm
149 °F

@Thickness 0.236 in
UL 746
Flammability, UL94 V-1

@Thickness 1.70 mm
V-1

@Thickness 0.0669 in
V-1

@Thickness 3.00 mm
V-1

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 3.10e+16 ohm-cm
3.10e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 216 - 266 °C
420 - 510 °F
Middle Barrel Temperature 227 - 271 °C
440 - 520 °F
Front Barrel Temperature 238 - 277 °C
460 - 530 °F
Melt Temperature 249 - 277 °C
480 - 530 °F
Mold Temperature 54.4 - 76.7 °C
130 - 170 °F
Drying Temperature 76.7 - 82.2 °C
170 - 180 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001