Asahi Kasei Thermofil P-40TC-2767 40% Talc Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermofil |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermofil P-40TC-2767 40% Talc Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 29.0 MPa | 4200 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 44.8 MPa | 6500 psi | ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm | 4.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3860 TPE, PP Overmold or Standalone use
- Resin Technology Group Fusion 830 General Purpose Fusion Cyanoacrylate
- Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **)
- Solvay Engineered Polymers SEQUEL® 1485 Engineered Polyolefin (discontinued **)
- Menzolit Menzolit® BMC 2400 Unsaturated Polyester UP
- Struktol POLYDIS 3691 Elastomer modified epoxy prepolymer
- Dow Fulcrum™ Thermoplastic Glass-Filled Polyurethane Composite Rod
- Bohler-Uddeholm UDDEHOLM ORVAR® SUPERIOR (Premium AISI H13) Hot Work Tool Steel
- BASF Ultramid® A3WG7 HP BK 20560 35% Glass Filled PA66 (Conditioned)
- Asahi Kasei Tenac® SH410 Homopolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved