Polymer Resources NY6-IM1-[color]H Nylon, Impact Modified, Heat Stabilized (DAM)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources NY6-IM1-[color]H Nylon, Impact Modified, Heat Stabilized (DAM).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.09 g/cc	0.0394 lb/in³	ASTM D792
Linear Mold Shrinkage	0.016 - 0.020 cm/cm	0.016 - 0.020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	62.1 MPa	9000 psi	ASTM D638
Tensile Strength, Yield	62.1 MPa	9000 psi	ASTM D638
Flexural Strength	75.8 MPa	11000 psi	ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	168 °C	335 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	62.8 °C	145 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in

Processing Properties	Metric	English
Rear Barrel Temperature	221 - 246 °C	430 - 475 °F
Middle Barrel Temperature	238 - 254 °C	460 - 490 °F
Front Barrel Temperature	243 - 260 °C	470 - 500 °F
Melt Temperature	238 - 268 °C	460 - 515 °F
Mold Temperature	65.6 - 82.2 °C	150 - 180 °F
Drying Temperature	73.9 - 85.0 °C	165 - 185 °F
Dry Time	3 - 4 hour	3 - 4 hour