Braskem LL118 Blown Film Extrusion Linear Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem LL118 Blown Film Extrusion Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: LL218/21 is a LLDPE Butene copolymer produced by Braskem. It was specially designed to provide outstanding processing performance. Films obtained with this grade show good physical and optical properties and enhanced sealability.Additive: Antiblocking Medium and Slip MédiumApplications: Stretch films; Liners; LDPE and HDPE blends; Packages for general use.Information provided by Braskem.
Physical Properties Metric English Comments
Specific Gravity 0.917 g/cc
0.917 g/cc
ASTM D1505/D792
Thickness 25.0 microns
0.984 mil
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 1140 %
1140 %
ASTM D882
Film Elongation at Break, TD 1440 %
1440 %
ASTM D882
Elmendorf Tear Strength MD 140 g
140 g
gF; ASTM D1922
Elmendorf Tear Strength TD 340 g
340 g
gF; ASTM D1922
Dart Drop Test 100 g
0.221 lb
gF/50%f; ASTM D1709
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
Ultimate; ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
Ultimate; ASTM D882
1% Secant Modulus, MD 200 MPa
29000 psi
ASTM D882
1% Secant Modulus, TD 220 MPa
31900 psi
ASTM D882
Optical Properties Metric English Comments
Gloss 24 %

@Thickness 0.0250 mm
24 %

@Thickness 0.000984 in
60°; ASTM D2457