Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.6 MPa
9800 psi
ASTM D638
Tensile Strength, Yield 67.6 MPa
9800 psi
ASTM D638
Flexural Strength 94.80 MPa
13750 psi
ASTM D790
Flexural Modulus 2.83 GPa
410 ksi
ASTM D790
Izod Impact, Notched 1.17 J/cm
2.20 ft-lb/in
ASTM D256
Gardner Impact >= 22.6 J
>= 16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
215 °F
ASTM D648
Flammability, UL94 HB
HB
1/16 in
Processing Properties Metric English Comments
Rear Barrel Temperature 193 - 204 °C
380 - 400 °F
Middle Barrel Temperature 196 - 207 °C
385 - 405 °F
Front Barrel Temperature 199 - 210 °C
390 - 410 °F
Melt Temperature 199 - 210 °C
390 - 410 °F
Mold Temperature 79.4 - 98.9 °C
175 - 210 °F
Drying Temperature 76.7 - 82.2 °C
170 - 180 °F
Dry Time 2 - 4 hour
2 - 4 hour