- Polykemi AB SCANTEC PC S75R V0 Polycarbonate, Flame Retardant
Polykemi AB SCANTEC PC S75R V0 Polycarbonate, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | SCANTEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANTEC PC S75R V0 Polycarbonate, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | With Flow; ISO 2577 |
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 60.0 MPa | <= 8700 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 105 MPa | <= 15200 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 140 °C @Load 5.001 kg |
284 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- RheTech Products FT4700-00A Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- PolyOne FireCon™ CPE 32-33 RoHS Black Polyethylene, Chlorinated (CPE)
- 3M Dyneon™ CC191-HE PTFE, 25% Carbon/Graphite Filled (discontinued **)
- Teknor Apex APEX® 94-A0098C-45 Polyvinyl Chloride, Flexible
- Zeon Chemicals Hydrin® T3106 Polyepichlorohydrin Elastomer
- DSM Novamid® 1010GH30 NAT PA6-GF30
- Carmel Olefins CAPILENE® E 65 F Polypropylene Homopolymer
- Ashley Polymers Ashlene® 68MG Nylon 66, Glass/Mineral reinforced
- Ceradyne SEMICORE® S1-5A MMOA 20/15 SmCo5 Samarium Cobalt Magnet
- Sylvin Technologies 9604-95 LMW Clear PVC for Injection Molding
Copyright © lookpolymers.com All Rights Reserved