- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Polymer Resources ABS-G5 ABS, 5% Glass Reinforced
Polymer Resources ABS-G5 ABS, 5% Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources ABS-G5 ABS, 5% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Acrylonitrile Butadiene Styrene, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.7 MPa | 6200 psi | ASTM D638 |
| Tensile Strength, Yield | 45.5 MPa | 6600 psi | ASTM D638 |
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 210 - 221 °C | 410 - 430 °F | |
| Front Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Melt Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 48.9 - 60.0 °C | 120 - 140 °F | |
| Drying Temperature | 79.4 - 85.0 °C | 175 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.001 |
Users viewing this material also viewed the following:
- Noltex Soarnol® ST110 Ethylene Vinyl Alcohol Copolymer
- Inhance Fluoro-Seal INHANCE® UH-1700 Ultra High Molecular Weight Polyethylene
- Karina E 856-08/151-Y-ERYB Beige PVC Compound
- Lavergne VYPET VNT 1021 Polyester-PC Alloy
- Shinkong Synthetic Fibers Shinite® PP4410 PP, Fire Retardant
- UBE 1022C2 NCH Nylon 6 Film
- A. Schulman POLYBATCH™ Canyon 10290U/4 Concentrate Based In LLDPE
- ConocoPhillips ANDEROL® FGH 22 Synthetic Food Grade Hydraulic Fluid, ISO 22
- Atom Adhesives AA-DUCT AD1 Epoxy Adhesive
- Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Conditioned, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved