- ITW Devcon Plastic Steel® Metal Repair 5 Minute® Putty (SF), Dark Grey
ITW Devcon Plastic Steel® Metal Repair 5 Minute® Putty (SF), Dark Grey
| Category | Polymer , Adhesive , Thermoset |
| Manufacturer | ITW Devcon |
| Trade Name | Plastic Steel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ITW Devcon Plastic Steel® Metal Repair 5 Minute® Putty (SF), Dark Grey.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by ITW Devcon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.27 g/cc | 0.0820 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | Cured; ASTM D2240 |
| Tensile Strength at Break | 21.4 MPa | 3100 psi | ASTM D638 |
| Modulus of Elasticity | 5.17 GPa | 750 ksi | ASTM D638 |
| Flexural Strength | 53.0 MPa | 7680 psi | ASTM D790 |
| Compressive Strength | 71.7 MPa | 10400 psi | ASTM D695 |
| Adhesive Bond Strength | 13.97 MPa | 2026 psi | tensile shear; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 61.2 µm/m-°C @Temperature 20.0 °C |
34.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 1.11 W/m-K | 7.68 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | dry |
| Shrinkage | 0.060 % | 0.060 % | Cured; ASTM D2566 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 35 @Frequency 1000 Hz |
35 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 1.18 kV/mm | 30.0 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min | 1.00 hour | Functional cure |
| Pot Life | 5.00 min @Temperature 23.9 °C |
5.00 min @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage per pound, in² @ 1/4" thickness | 49 | |
| Mix ratio by volume (Resin:Hardener) | 1:1 | |
| Mix ratio by weight (Resin:Hardener) | 1.7:1 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8192 (826-1) (UF) Synthetic Oil
- Precision Polymer Engineering N65E Nitrile Rubber
- Polykemi AB POLYelast TPE Z600 Thermoplastic Elastomer, SEBS-based
- Resinlab® CYNERGY CA6006 Adhesive
- Lehmann & Voss LUVOCOM® 1-8491 Polyamide 66, with carbon fiber, heat stabilized
- Michelman® Licomer® W 315 FP Anionic / Nonionic polyethylene emulsion
- Sharadaa Ceramics 0.5 Insulation Brick
- Borealis Borcoat™ HE3450 Black High Density Polyethylene Top Coat for Steel Pipe Coating
- Tipco Tipcolene® NPI 200 IN - 25% Talc/Mineral Reinforced Polypropylene Copolymer with Very High Flow, Stiffness & Impact Strength
Copyright © lookpolymers.com All Rights Reserved