Polykemi AB POLYfill PPH TS5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPH TS5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Filler Content 40 %
40 %
±2%; Polykemi
Linear Mold Shrinkage 0.0090 - 0.011 cm/cm
0.0090 - 0.011 in/in
With Flow; ISO 2577
0.0090 - 0.011 cm/cm
0.0090 - 0.011 in/in
Across Flow; ISO 2577
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 28.0 MPa
<= 4060 psi
ISO/R527
Elongation at Yield 5.0 %
5.0 %
ISO/R527
Flexural Strength <= 54.0 MPa
<= 7830 psi
ISO 178
Flexural Modulus 3.20 GPa

@Temperature 23.0 °C
 464 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.300 J/cm²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 122 °C
252 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
120°C/h; ISO 75/1
Vicat Softening Point 84.0 °C

@Load 5.001 kg
 183 °F

@Load 11.03 lb
 50°C/h; ISO 306
146 °C

@Load 1.00 kg
 295 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 IEC 695-2-1
Processing Properties Metric English Comments
Melt Temperature 205 - 260 °C
401 - 500 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2 - 4 hour
2 - 4 hour
in circulation dryer
2 - 4 hour
2 - 4 hour
in desiccant air dryer
Injection Pressure 40.0 - 110 MPa
5800 - 16000 psi
Back Pressure 1.00 - 2.00 MPa
145 - 290 psi
Descriptive Properties Value Comments
Holding Pressure () 20-40
% of injection pressure
Injection Speed () High