Grupo Repol Dinalon® A1S25 PA66 Unreinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® A1S25 PA66 Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75/A |
| Vicat Softening Point | >= 230 °C | >= 446 °F | 50N; ISO 306 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2103-20 CR-SX Fiberglass Reinforced Thermoset BMC
- ExxonMobil Exceed™ 1327CA Blown Film Resin (discontinued **)
- Lubriplate Super HDS L0789 Motor Oil Motor Oil & Transmission Fluid
- KYDEX® 331/331d Co-Extruded High Impact Fire Rated Thermoplastic Sheet with Weatherable Acrylic Film Cap
- Sekisui PIOCELAN OP-E30ENS (Antistatic) Moldable Polymer Foam
- Loctite® 3171 Deep Potting Polyurethane
- Ensinger Tecapeek® XP-97 Compression Molded PEEK Compound, 30% Graphite Filled
- Lehmann & Voss LUVOCOM® 1301-8305 PPS, linear, with glass fiber, lubricant modified
- Unitika EX-1222 PA6, Conditioned
Copyright © lookpolymers.com All Rights Reserved