Polykemi AB POLYfill PPH T5040 FC Polypropylene Homopolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Polykemi AB POLYfill PPH T5040 FC Polypropylene Homopolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Filler Content | 40 % | 40 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 | |
| Melt Index of Compound | 5.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
5.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO/R527 |
| Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
| Flexural Modulus | 3.80 GPa <br>@Temperature 23.0 °C |
551 ksi <br>@Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² <br>@Temperature -40.0 °C |
1.43 ft-lb/in² <br>@Temperature -40.0 °F |
ISO 180/4A |
| 5.00 kJ/m² <br>@Temperature 23.0 °C |
2.38 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 180/4A | |
| Charpy Impact, Notched | 0.200 J/cm² <br>@Temperature -20.0 °C |
0.952 ft-lb/in² <br>@Temperature -4.00 °F |
ISO 179 |
| 0.300 J/cm² <br>@Temperature 23.0 °C |
1.43 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 89.0 °C <br>@Load 5.001 kg |
192 °F <br>@Load 11.03 lb |
50°C/h; ISO 306 |
| 150 °C <br>@Load 1.00 kg |
302 °F <br>@Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB <br>@Thickness 1.60 mm |
HB <br>@Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C <br>@Thickness 2.00 mm |
1380 °F <br>@Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs R00 ABS, High Impact
- Momentive Performance Materials AC6043 Titanium Diboride/Boron Nitride Composite
- Momentive Performance Materials IS803 Black Adhesive Sealant, General Purpose Paste
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 20 lb
- Borealis Daplen™ EG102AI Polypropylene Compound 15% Mineral Filled
- Master Bond Supreme 33CLV Two Component, Room Temperature Curing Toughened Epoxy
- BASF Lupranate® 5100 Isocyanate
- Total LDPE 1022 FN 24 Low Density Polyethylene - Blown Film
- Arlon 55090R028 0.028 (0.711 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved