Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.86 g/cc | 0.0672 lb/in³ | ISO 1183 |
| Filler Content | 65 % | 65 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | With Flow; ISO 2577 |
| 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 18.0 MPa | <= 2610 psi | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 100 °C @Load 5.001 kg |
212 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 150 °C @Load 1.00 kg |
302 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Impact Modified 4120 HS Nylon 6/6; MoS2 lube
- Pau Tai UNISTAB RP-220 Solid Complex Stabilizer
- Chevron Phillips HiD® 9502/HiD® 9503 with Antistat HDPE Blow Molding Resin (discontinued **)
- Gromax BFG10-BN00N1 Nylon 6 10% Glass Filled (Dry)
- Total LLDPE LL 1810 H Linear Low Density Polyethylene - Blown Film
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Black Peroxide Cure
- Fainplast Compounds HAX HF 3522D Halogen Free PVC
- Braskem H 504 XP Bioriented Film Polypropylene
- Bhansali Engineering Abstron IM14GL ABS Injection Molding Grade
- 3M Scotchcal™ 1000-54 Graphic Film
Copyright © lookpolymers.com All Rights Reserved