- Polykemi AB POLYfill PPC TS4030 H Polypropylene Copolymer, Mineral Reinforced
Polykemi AB POLYfill PPC TS4030 H Polypropylene Copolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 30% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPC TS4030 H Polypropylene Copolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 @Time 15.0 sec |
64 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 25.0 MPa | <= 3630 psi | ISO/R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 36.0 MPa | <= 5220 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa @Temperature 23.0 °C |
276 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 76.0 °C @Load 5.001 kg |
169 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 142 °C @Load 1.00 kg |
288 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- M. Holland Company PP500 Polypropylene Homopolymer
- Fibre Glast 543 Style 7781 E-Glass Fiberglass Fabric
- Latrobe Lescalloy® Jethete M-152 ESR 2.25" RD High Strength Stainless Steel
- Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA), 65% GlassMineral (Conditioned)
- Techmer ES HiFill® PA6 GF33 HS L 33% Glass Filled
- Borealis Daplen™ EE065AI Polypropylene Elastomer Modified
- A. Schulman POLYBATCH™ Grey 8760 Concentrate Based In Polyethylene
- DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer
- Arkema Group LOTRYL® 15 MA 03 Copolymer Ethylene - Methyl Acrylate
- PSM Industries Pacific Sintered Metals Yellow Brass BZ-111-UC Powdered Metal
Copyright © lookpolymers.com All Rights Reserved