- Polykemi AB POLYfill PP HJ752 Polypropylene/Elastomer, Mineral Reinforced
Polykemi AB POLYfill PP HJ752 Polypropylene/Elastomer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP HJ752 Polypropylene/Elastomer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
| Elongation at Break | 167 % | 167 % | ISO/R527 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO/R527 |
| Flexural Strength | <= 32.0 MPa | <= 4640 psi | ISO 178 |
| Flexural Modulus | 1.70 GPa @Temperature 23.0 °C |
247 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 2.30 J/cm² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 - 65.0 µm/m-°C | 30.6 - 36.1 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 53.0 °C @Load 5.001 kg |
127 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 130 °C @Load 1.00 kg |
266 °F @Load 2.21 lb |
50°C/h; ISO 306 |
Users viewing this material also viewed the following:
- Oceanchem Group Tetrabromobisphenol A (TBBA)
- SABIC Innovative Plastics Cycoloy® XCM830 PC+ABS (Europe-Africa-Middle East)
- Polykemi AB POLYfill PPH GF8020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Victrex® Vicote® F806 Polyetheretherketone (PEEK) Liquid Dispersion
- FKuR Kunststoff Bio-Flex® S 6540 Compostable PLA Blend
- LG Chemical DIDP Plasticizer
- Dow Corning SILASTIC® 9251/45 A&B KIT
- ExxonMobil Oppalyte™ 38DO447 OPP Film
- Colorite Polymers 10014G-015 (Molding) Radiation Sterilizable Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved