Polykemi AB POLYfill PP CQX10030E10 Polypropylene, Mineral Reinforced, Elastomer Modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP CQX10030E10 Polypropylene, Mineral Reinforced, Elastomer Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | With Flow; ISO 2577 |
| 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 19.0 MPa | <= 2760 psi | ISO/R527 |
| Elongation at Break | 23 % | 23 % | ISO/R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
| Flexural Modulus | 1.70 GPa @Temperature 23.0 °C |
247 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -20.0 °C |
21.4 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 90.0 µm/m-°C | 38.9 - 50.0 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 70.0 °C @Load 5.001 kg |
158 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 144 °C @Load 1.00 kg |
291 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 70.0 MPa | 5800 - 10200 psi | |
| Back Pressure | 1.00 - 1.50 MPa | 145 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | > 40 | % of injection pressure |
| Injection Speed () | High | |
| Scratch Resistance, 10N (dL) | < 0.1 | 10 N Fine structure; ISO 1518/D65 |
Users viewing this material also viewed the following:
- Nylacast Nylube MO Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant), MoS2 Filled
- PolyOne Edgetek® ES-40CF/000 Polyethersulfone - 40% Carbon Fiber Reinforced (discontinued **)
- Pasargad Polymer Peyvand Pasamid 3P-H1150B Nylon 6, 50% Glass Fiber Reinforced
- Ineos ABS Centrex® 814 ASA Blend (discontinued **)
- Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Dry)
- Special Metals INCONEL® alloy 740 Precipitation-Hardenable Ni-Cr-Co Superalloy
- Unitika elitel UE3370 Polyester, Flake
- Total HDPE 53090 High Density Polyethylene - Blow Molding
- A. Schulman POLYBATCH™ White HS8350 Concentrate Based In Impact Polystyrene
- Cossa Polimeri ESTASTIR HI 0810 V0 Flame Retardant Polystyrene
Copyright © lookpolymers.com All Rights Reserved