- Polymer Property : Tensile Strength at Break = 2760 psi
Polymer Property : Tensile Strength at Break = 2760 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| SABIC R40039E Medium Density Polyethylene for Rotational Molding Product Description: R40039E is a Medium Density Polyethylene grade designed to provide excellent mechanical properties with high rigidity, toughness, gloss and low warpage. R40039E is UV stabiliz.. |
|||
| Tensile Strength at Break | 19.0 - 29.0 MPa @Temperature 23.0 °C |
2760 - 4210 psi @Temperature 73.4 °F |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Halar® 1400LC Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**) Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | after 7days @113°C; UL 1581 |
| SABIC Innovative Plastics NORYL WCD861A PPE-TPE Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Silon Taborex TA 1134 HD Chemically-Crosslinkable HDPE Compound TABOREX TA 1134 HD is a crosslinkable compound made of Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a “SIOPLA.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East) LNP* STARFLAM* MX96070 is a compound based on Polypropylene resin containing Flame Retardant. Added features include: Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middl.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific) LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Tensile Strength at Break | 19.0 MPa @Treatment Temp. 145 °C, Time 2100 sec |
2760 psi @Treatment Temp. 293 °F, Time 0.583 hour |
Cure; ASTM D412 |
| Styron Sprintan® SLR 4630 Solution Styrene Butadiene Rubber (S-SBR) Composition: SPRINTAN® SLR-4630 – Schkopau is manufactured by anionic solution polymerization using an organo-lithium initiator. In relation to solid rubber the grade is extended with 37.5 p.. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | |
| Sibur BK-1675N Butyl Rubber (IIR) EXXON Butyl 268, PB 301 Bayer. For production of automobile inner tubes, heating tubes, sharper vulcanizer diaphragms, and rubber fabrics. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| UBE V206 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| UBE V210 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO 527-2 |
| Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
| Tensile Strength at Break | 19.0 - 22.0 MPa | 2760 - 3190 psi | ASTM D638 |
| Daikin NEOFLON NP-130 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Heavy wall wire insulation, cable jacketing, pipe, shrinka.. |
|||
| Tensile Strength at Break | 19.03 MPa | 2760 psi | JIS-K-6723 |
| Denka VINYKON W7300E PVC, W grade for non-migratory sheath and special items A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding.. |
|||
| Tensile Strength at Break | 19.0 - 22.0 MPa | 2760 - 3190 psi | ASTM D638 |
| Daikin NEOFLON NP-20 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, injection molding.Applications: Wire and cable coatings, films,.. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ISO R 527 |
| Fainplast Compounds FR 95/1 Flexible PVC, Insulation General purposes |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Fainplast Compounds PG 86/AF Flexible PVC, Extrusion Modified with Rubber Profiels UL 94 Classe V0 |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Fainplast Compounds PHA 91 Flexible PVC, Transparent Extrusion Atoxic pipes |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Fainplast Compounds PHT 0144 Flexible PVC, Transparent Extrusion Profiles high temperatures |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0339C40L1 Calcium Reinforced |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ASTM D4894 |
| Adamas Adalon® 215 PTFE, 17% Glass Filled, Blue Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM-D638 |
| Braskem PN2021 EVA Foam Copolymer PN2021 is an Ethylene-Vinyl Acetate (EVA) copolymer mainly used for the production of crosslinked/expanded plates and other parts. It is a product with easy processability and high compatibility wit.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM-D638 |
| Braskem TN2020 EVA General Film Copolymer TN2020 is an Ethylene-Vinyl Acetate (EVA) copolymer developed to mostly meet the needs of the multi-layer packaging segment produced by coextrusion and/or lamination processes. Multilayer structures.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Addiplast Addilene H 532 N30 Polypropylene Homopolymer Good surface appearanceInformation provided by Addiplast. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ISO R 527 |
| Fainplast Compounds CKL 63/K Flexible PVC, Sheathing Lead Free Opaque sheath |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Fainplast Compounds PH 90/A Flexible PVC, Transparent Extrusion Profiles, UL 94 Class V1 |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO 527-2 |
| Total Lacqrene® 814(EU) High Impact Polystyrene
(discontinued **) LACQRENE® 814 is a PBDE free high impact, flame retardant polystyrene with excellent UV stability, rated UL 94 V0 @ 2mm and UL 94 5 VA @ 3mm.ApplicationCovers for electrical equipment, External cov.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W2402 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||