- Polykemi AB POLYelast TPE Z706EX Thermoplastic Elastomer, SEBS-based
Polykemi AB POLYelast TPE Z706EX Thermoplastic Elastomer, SEBS-based
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z706EX Thermoplastic Elastomer, SEBS-based.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | With Flow; ISO 2577 |
| 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | <= 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
<= 1.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 @Time 15.0 sec |
70 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 9.50 MPa | <= 1380 psi | ISO/R527 |
| Elongation at Break | 650 % | 650 % | ISO/R527 |
| 100% Modulus | 0.00220 GPa | 0.319 ksi | ISO/R527 |
| 300% Modulus | 0.00400 GPa | 0.580 ksi | ISO/R527 |
| Tear Strength | 32.0 kN/m | 183 pli | D624 |
| Compression Set | 28 % @Temperature 23.0 °C, Time 259000 sec |
28 % @Temperature 73.4 °F, Time 72.0 hour |
DIN 53517 |
| 50 % @Temperature 70.0 °C, Time 86400 sec |
50 % @Temperature 158 °F, Time 24.0 hour |
DIN 53517 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- LG Chemical LUMID HI5063A(W) PA6/ABS+MF6%, High Impact
- Haynes 282® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
- Solvay Specialty Polymers Ryton® R-7-220BL Polyphenylene Sulfide (PPS), GlassMineral Filled
- Bond Laminates TEPEX® dynalite 102-RG600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate
- BASF Lupragen® N 107 Dimethylaminoethoxyethanol
- Arkema Group Lacovyl® PA 1384 Vinyl Copolymer
- 3M Scotch-Weld™ 3748 VO Hot Melt Adhesive
- LATI LARAMID G/45 45% Glass Filled Polyphthalamide (PPA) Based Compound (Unverified Data**)
- RheTech Products GC43P250-01 43% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black
Copyright © lookpolymers.com All Rights Reserved