PolyOne Lubri-Tech™ NI-10CF/15T Nylon 6/10, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ NI-10CF/15T Nylon 6/10, Carbon Fiber Reinforced, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 121 MPa | 17500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 1000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10000 ohm | 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 282 °C | 480 - 540 °F | Molding |
| Mold Temperature | 93.3 - 104 °C | 200 - 220 °F | |
| Drying Temperature | 93.3 - 104 °C | 200 - 220 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Abatron AboCast 8-8/Abocure 8-8 Epoxy (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7353/NAT Polyacetal-copolymer, with aramid reinforcement and PTFE
- SABIC Innovative Plastics LNP STAT-KON DD000 PC (Europe-Africa-Middle East)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 80 PHR Dixie Clay Filler
- Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating
- Abatron AboCrete Cement/Grout Resurfacing and Patching Epoxy
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 60% Cold Rolled (UNS S30403)
Copyright © lookpolymers.com All Rights Reserved