Polycasa Acryl® KR 2006/1 Acrylic, Impact Grade

Category	Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded
Manufacturer	Polycasa
Trade Name	Acryl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polycasa Acryl® KR 2006/1 Acrylic, Impact Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Impact-modified grade for highly stressed parts; highest impact and notched-impact resistance; can be mixed with general-purpose grades to get the desired toughness; highly resistant to stress cracking.Data was collected by ISO methods.Quinn Manufacturing Group rebranded its Plastics Division as Polycasa in 2013.

Physical Properties	Metric	English
Density	1.14 g/cc	0.0412 lb/in³
Moisture Absorption at Equilibrium	0.40 %	0.40 %
Linear Mold Shrinkage, Flow	0.0065 cm/cm	0.0065 in/in
Melt Flow	0.90 g/10 min @Load 3.80 kg, Temperature 230 °C	0.90 g/10 min @Load 8.38 lb, Temperature 446 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	45.0 MPa	6530 psi
Elongation at Break	45 %	45 %
Elongation at Yield	5.0 %	5.0 %
Tensile Modulus	1.80 GPa	261 ksi
Charpy Impact Unnotched	8.00 J/cm²	38.1 ft-lb/in²
Charpy Impact, Notched	0.700 J/cm²	3.33 ft-lb/in²

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	110 µm/m-°C @Temperature 20.0 °C	61.1 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F
Vicat Softening Point	98.0 °C	208 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
Oxygen Index	18 %	18 %

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
	3.2 @Frequency 100 Hz	3.2 @Frequency 100 Hz
Dielectric Strength	60.0 kV/mm	1520 kV/in
Dissipation Factor	0.030 @Frequency 1e+6 Hz	0.030 @Frequency 1e+6 Hz
	0.040 @Frequency 100 Hz	0.040 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V