Chesterton ARC NVE SYSTEM Vinyl Ester Lining

Category Polymer , Thermoset , Vinyl Ester
Manufacturer Chesterton
Trade Name ARC NVE SYSTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton ARC NVE SYSTEM Vinyl Ester Lining.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ARC NVE is a high performance, quartz reinforced, three-component, modified novolac vinyl ester lining capable of being applied to horizontal and vertical surfaces. The NVE system kit is comprised of a primer (NVE PC), top coat (NVE TC) and optional veil coat sealer (NVE VC) which is used in applications that require high impact and abrasion resistance combined with resistance to a wide range of solvents, acids, fats, oils, water and various chemicals at ambient as well as elevated temperatures. Benefits:Deep penetrating primer system allows for exceptionally high adhesion to prepared concreteIntegrated topcoat sealer system prevents migration or penetration of chemicalsHigh quartz loading ensure a compatible thermal coefficient of expansion providing long-term resistance to disbondment.Graded quartz reinforcements allow for single lift vertical build application up to 3 meters (10 ft)User friendly consistency makes installation and finishing fast and easy.Applications: ARC NVE is generally used to repair and upgrade concrete surfaces or as a replacement for acid resistant tiles, phenolics, furans, conventional novalac epoxy, sulfonated concretes and other overlayments. It is formulated to be thermally compatible with concrete and its rapid curing allows areas to be returned to service in as little as 24 hours. ARC NVE is chosen over the ARC Concrete Composite Systems for its superior chemical resistance.Suggested Uses:Battery RoomsPickling & Plating LinesBleaching AreasSumps, Trenches & PitsChemical ContainmentsPump & Equipment BasesChemical Loading StationsPickling RoomsCAS: 100-42-5Information provided by Chesterton
Physical Properties Metric English Comments
Density 2.24 g/cc
0.0809 lb/in³
Cured
Volatiles 2.2 %
2.2 %
EPA 24
Mechanical Properties Metric English Comments
Tensile Strength at Break 9.915 MPa
1438 psi
ASTM C307
Modulus of Elasticity 12.4 GPa
1800 ksi
Flexural
Flexural Strength 17.48 MPa
2535 psi
ASTM C580
Compressive Strength 78.6 MPa
11400 psi
ASTM C579
Adhesive Bond Strength >= 3.86 MPa
>= 560 psi
Excellent - 100% Concrete Failure
Thermal Properties Metric English Comments
CTE, linear 26.6 µm/m-°C
14.8 µin/in-°F
ASTM C531
Maximum Service Temperature, Air 135 °C
275 °F
Wet Continuous
200 °C
392 °F
Dry Continuous
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 26.0 °C
1.00 hour

@Temperature 78.8 °F
Foot Traffic
60.0 min

@Temperature 26.0 °C
1.00 hour

@Temperature 78.8 °F
Light Load
60.0 min

@Temperature 26.0 °C
1.00 hour

@Temperature 78.8 °F
Full Load
90.0 min

@Temperature 21.0 °C
1.50 hour

@Temperature 69.8 °F
Foot Traffic
90.0 min

@Temperature 21.0 °C
1.50 hour

@Temperature 69.8 °F
Light Load
120 min

@Temperature 21.0 °C
2.00 hour

@Temperature 69.8 °F
Full Load
150 min

@Temperature 16.0 °C
2.50 hour

@Temperature 60.8 °F
Foot Traffic
180 min

@Temperature 16.0 °C
3.00 hour

@Temperature 60.8 °F
Light Load
240 min

@Temperature 10.0 °C
4.00 hour

@Temperature 50.0 °F
Foot Traffic
240 min

@Temperature 16.0 °C
4.00 hour

@Temperature 60.8 °F
Full Load
360 min

@Temperature 10.0 °C
6.00 hour

@Temperature 50.0 °F
Light Load
480 min

@Temperature 10.0 °C
8.00 hour

@Temperature 50.0 °F
Full Load
960 min

@Temperature 26.0 °C
16.0 hour

@Temperature 78.8 °F
Full Chemical
1440 min

@Temperature 21.0 °C
24.0 hour

@Temperature 69.8 °F
Full Chemical
1680 min

@Temperature 16.0 °C
28.0 hour

@Temperature 60.8 °F
Full Chemical
1920 min

@Temperature 10.0 °C
32.0 hour

@Temperature 50.0 °F
Full Chemical
Descriptive Properties Value Comments
Color Gray
Red
Thermal Compatibility to Concrete Pass
ASTM C884