Dow Corning EG-6301
| Category | Polymer , Adhesive , Thermoset , Silicone |
| Manufacturer | Dow Corning |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Corning EG-6301.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Two-part, transparent, high modulus (hard) LED encapsulant with high transparency and very long working time.Information provided by Dow Corning
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 71 | 71 | |
| Tensile Strength, Ultimate | 8.9997 MPa | 1305.3 psi | |
| Elongation at Break | 80 % | 80 % | |
| Modulus of Elasticity | 0.006700 GPa | 0.9718 ksi |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.403 | 1.403 | |
| 1.411 | 1.411 | ||
| 1.402 @Wavelength 1554 nm |
1.402 @Wavelength 1554 nm |
||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min @Temperature 150 °C |
1.00 hour @Temperature 302 °F |
|
| Shelf Life | 6.00 Month | 6.00 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio (X:1) | 100 | Base to Catalyst ETN |
Users viewing this material also viewed the following:
- Petroquimica Triunfo Trilene® TS 8057 LLDPE-C4 and LDPE Blend
- GrafTech P1 PET Film
- Huntsman AVALON® 70 ABX Thermoplastic Polyurethane
- Materion Alloy M65 (C17465) Beryllium Copper Rod
- Eastman Tenite 307E4000018 Propionate Clear, Trsp
- ELASTO UK Dryflex® 600700S SEBS Based Material, Filled Qualities, 70A Hardness, Natural
- Fainplast Compounds FR 95 Flexible PVC, Insulation
- A. Schulman ComAlloy Hiloy® 247 SAN, Glass/Mineral Reinforced, UL
- Tra-Con Tra-Duct 2929 Room Temperature Conductive Flexible Silver Epoxy Adhesive
- Mateck Sapphire Aluminium oxide Substrate, Al2O3
Copyright © lookpolymers.com All Rights Reserved