SABIC Innovative Plastics LNP THERMOCOMP UF004AS PPA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP UF004AS PPA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* UF004AS is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 136 MPa
19700 psi
5 mm/min; ISO 527
Elongation at Break 1.7 %
1.7 %
5 mm/min; ISO 527
Tensile Modulus 7.50 GPa
1090 ksi
1 mm/min; ISO 527
Flexural Strength 178 MPa
25800 psi
2 mm/min; ISO 178
Flexural Modulus 7.00 GPa
1020 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 31.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 17.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 256 °C
493 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af