Toyobo PELPRENE™ P55U Polyester TPE, Weather-resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P55U Polyester TPE, Weather-resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Weather-resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.45 % | 0.45 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 22 g/10 min @Temperature 230 °C |
22 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 94 | 94 | JIS K6301 |
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| 50% Modulus | 0.00980 GPa | 1.42 ksi | ASTM D638 |
| Flexural Modulus | 0.0760 GPa | 11.0 ksi | ASTM D790 |
| Compressive Modulus | 0.00760 GPa | 1.10 ksi | 0.1; ASTM D695 |
| Resilience | 74 | 74 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 113 kN/m | 645 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | ASTM D1044 |
| Compression Set | 53 % | 53 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 182 °C | 360 °F | By DSC |
| Maximum Service Temperature, Air | <= 25.0 °C | <= 77.0 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 155 °C | 311 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+12 ohm-cm | 9.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C6850REC PC+ABS (Europe-Africa-Middle East)
- NIZHNEKAMSKNEFTEKHIM PE 4152L (524F6) High Density Polyethylene
- Permabond ES578 Epoxy Resin
- Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled
- Rotuba M Cellulose Acetate
- PolyOne Dynaflex™ G6713C Thermoplastic Elastomer (TPE)
- Kazanorgsintez 102-05K Cable Composition Based on Low Density Polyethylene
- A. Schulman POLYBATCH™ U-7000-HS Blowing Agent Concentrate Based In HIPS
- C.O.I.M. EXTER S® S 901 Special Laminate
- Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C (discontinued **)&l
Copyright © lookpolymers.com All Rights Reserved