PolyOne Stat-Tech™ NJ-20CF/000 Black Polyamide 12 (Nylon 12)

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ NJ-20CF/000 Black Polyamide 12 (Nylon 12).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.11 g/cc	1.11 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.00050 - 0.0020 cm/cm	0.00050 - 0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.00050 - 0.0020 cm/cm	0.00050 - 0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	119 MPa	17300 psi	ASTM D638
Elongation at Break	5.2 %	5.2 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	8.00 GPa	1160 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	192 MPa	27800 psi	ASTM D790
Flexural Modulus	8.07 GPa	1170 ksi	ASTM D790
Izod Impact, Notched	1.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.44 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	175 °C @Thickness 6.35 mm	347 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	163 °C @Thickness 6.35 mm	325 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1000 ohm-cm - 1e+05	1000 ohm-cm - 1e+05	ASTM D257
Surface Resistance	1000 ohm - 1e+05	1000 ohm - 1e+05	ASTM D257
Static Decay	0.0020 sec	0.0020 sec	(Mil-B-81705C), 12% RH, 5000 kV to 50 kV

Processing Properties	Metric	English	Comments
Melt Temperature	254 - 277 °C	489 - 531 °F

Descriptive Properties	Value	Comments
Features	Good Chemical Resistance
	Good Stability
	Low to No Water Absorption
Filler / Reinforcement	Carbon Fiber Reinforcement, 20% Filler by Weight
Forms	Pellets
Generic Material	Nylon 12
Generic Name	Polyamide 12 (Nylon 12)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Consumer Applications
	Electrical Housing
	Electrical/Electronic Applications
	Housings
	Marine Applications
	Sporting Goods