PolyOne OnForce™ LFT NN-50LGF/000 HS Black Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name OnForce™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne OnForce™ LFT NN-50LGF/000 HS Black Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A low shear process is advised, with low back pressure, low screw speed and low-to-medium injection speed.Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Measured on a tensile specimen.; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 250 MPa
36300 psi
ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527-2
Flexural Strength 310 MPa
45000 psi
ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
ISO 178
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
ISO 179
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Unannealed; ISO 75-2/A
Deflection Temperature at 8.0 MPa 227 °C
441 °F
Unannealed; ISO 75-2/C
Processing Properties Metric English Comments
Melt Temperature 290 - 320 °C
554 - 608 °F
Mold Temperature 90.0 °C
194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Back Pressure 1.00 MPa
145 psi
Descriptive Properties Value Comments
Features Heat Stabilized
Filler / Reinforcement Long Glass Fiber, 50% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Injection Rate Slow-Moderate
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America