SABIC Innovative Plastics LNP THERMOCOMP WF004 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WF004 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* WF004 is a compound based on PBT resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | 5 mm/min; ISO 527 |
| 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.4 % | 2.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D638 |
| 7.59 GPa | 1100 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 173 MPa | 25100 psi | ISO 178 |
| 182 MPa | 26400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 183 MPa | 26500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.66 GPa | 966 ksi | 2 mm/min; ISO 178 |
| 7.11 GPa | 1030 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.01 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 102 µm/m-°C @Temperature -30.0 - 30.0 °C |
56.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 781D (NG) Synthetic Oil
- PolyOne FireCon™ CPE 30-33 RoHS BLACK Polyethylene, Chlorinated (CPE)
- Indium Corp. CU 12 Copper Cleaner
- LyondellBasell Lupolen® 1812 E LDPE
- DuPont Elvaloy® 742 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
- A. Schulman POLYBATCH™ Yellow LL20203/2 Concentrate Based In LDPE
- ChevronTexaco HPLX SAE 30 Chevron HPLX Low Ash Gas Engine Oil
- Arkema Group Rilsan® AESN P40 TL Nylon 12, Flexible Tubing Grade (Conditioned)
- Aclo Accutech Polypropylene Copolymer CP0436C30L Calcium Reinforced
- LATI Latamid 66 H2 G/25-V0KB3 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved