- SABIC Innovative Plastics LNP KONDUIT OX11315 PPS (Asia Pacific)
SABIC Innovative Plastics LNP KONDUIT OX11315 PPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT OX11315 PPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermally conductive electrically insulative mineral filled PPS FR compound.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.010 % @Time 86400 sec |
<= 0.010 % @Time 24.0 hour |
SABIC Method |
| Moisture Absorption | <= 0.0100 % | <= 0.0100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00020 cm/cm @Time 86400 sec |
0.00020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.00030 cm/cm @Time 86400 sec |
0.00030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 0.40 % | 0.40 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 16.4 GPa | 2380 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 16.2 GPa | 2350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.150 J/cm | 0.281 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.30 µm/m-°C @Temperature 40.0 - 120 °C |
4.61 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 22.4 µm/m-°C @Temperature 40.0 - 120 °C |
12.4 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 |
| Specific Heat Capacity | 1.26 J/g-°C | 0.301 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 3.50 W/m-K | 24.3 BTU-in/hr-ft²-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 |
| 15.0 W/m-K | 104 BTU-in/hr-ft²-°F | in-plane, ø25*0.4mm disc; ASTM E 1461-07 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C @Thickness 6.40 mm |
442 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
UL 94 |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.40e+15 ohm | 2.40e+15 ohm | ASTM D257 |
| Dielectric Strength | >= 4.00 kV/mm @Thickness 1.00 mm |
>= 102 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Glass Filled 5105 HS Nylon 6/6
- Gharda Chemicals GATONE™ 5630FC Polyetheretherketone (PEEK) (discontinued **)
- SABIC M200024 Linear Low Density Polyethylene for Injection Molding
- Overview of materials for Polyphenylene Ether, PTFE Filled
- Momentive Performance Materials RTV108 Translucent Adhesive Sealant, High Strength Paste
- Materion Beryllium Copper Alloy M25 Wire; 3/4H (TD03) Temper; 1.3-2.0 mm Diameter (UNS C17300)
- A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass)
- Eurotec® Tecodur® PB70 GR15 NL TD 28 PBT 15% glass fiber reinforced, UL94 V0, impact modified, high CTI
- 3M FVS110S Static Cling Label Materials
- Albis Plastics Cellulose Acetate Butyrate B908 , 13% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved