PolyOne LubriOne™ GF-1010 40 MS 2 HS Black 37 Polyamide 6 (Nylon 6)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ GF-1010 40 MS 2 HS Black 37 Polyamide 6 (Nylon 6).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.41 g/cc	1.41 g/cc	ASTM D792
Water Absorption	0.70 %	0.70 %	@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.010 - 0.020 cm/cm	0.010 - 0.020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	122 MPa	17700 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield	122 MPa	17700 psi	ASTM D638
Elongation at Break	4.5 %	4.5 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	9.17 GPa	1330 ksi	ASTM D638
Flexural Strength	193 MPa	28000 psi	ASTM D790
Flexural Modulus	8.96 GPa	1300 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	3.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic	0.21	0.21	vs. Steel - Dynamic; ASTM D1894
Coefficient of Friction, Static	0.31	0.31	vs. Steel - Static; ASTM D1894

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	207 °C	405 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	185 °C	365 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	249 - 277 °C	480 - 531 °F
Mold Temperature	82.2 - 93.3 °C	180 - 200 °F
Drying Temperature	71.1 - 76.7 °C	160 - 170 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour

Descriptive Properties	Value	Comments
Appearance	Black
Features	Good Wear Resistance
	Heat Stabilized
	High Stiffness
	Nucleated
Forms	Pellets
Generic Material	Nylon 6
Generic Name	Polyamide 6 (Nylon 6)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Automotive Applications
	Bearings
	Business Equipment
	Consumer Applications
	Conveyor Parts
	Gears
	Industrial Applications
	Printer Parts
	Pulleys
	Rollers