EMS-Grivory Grivory® HTV-6H1 black 9205 PA6T/6I-GF60

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® HTV-6H1 black 9205 PA6T/6I-GF60.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Grivory HTV-6H1 black 9205 is a 60% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I. Acc. to ASTM: PPA, polyphthalamide. The main distinguishing feature of Grivory HT, when compared to other polyamides, is its good performance at high temperatures providing parts which are stiffer, stronger and have better heat distortion stability and chemical resistance. Grivory HT is suitable for production of technical parts in the application fields of:ElectroElectronicsAutomotiveMechanical engineeringDomestic applianceInformation provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Water Absorption 3.0 %
3.0 %
ISO 62
Moisture Absorption 1.20 %
1.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 360 MPa
52200 psi
dry; ISO 2039-1
360 MPa
52200 psi
conditioned; ISO 2039-1
Tensile Strength at Break 250 MPa
36300 psi
conditioned; ISO 527-1/-2
260 MPa
37700 psi
dry; ISO 527-1/-2
Elongation at Break 1.5 %
1.5 %
dry; ISO 527-1/-2
1.5 %
1.5 %
conditioned; ISO 527-1/-2
Tensile Modulus 22.5 GPa
3260 ksi
conditioned; ISO 527-1/-2
23.0 GPa
3340 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 7.50 J/cm²
35.7 ft-lb/in²
dry; ISO 179/1eU
7.50 J/cm²
35.7 ft-lb/in²
conditioned; ISO 179/1eU
7.50 J/cm²

@Temperature 30.0 °C
35.7 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
7.50 J/cm²

@Temperature 30.0 °C
35.7 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
dry; ISO 179/1eA
1.10 J/cm²
5.23 ft-lb/in²
conditioned; ISO 179/1eA
1.00 J/cm²

@Temperature 30.0 °C
4.76 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
1.00 J/cm²

@Temperature 30.0 °C
4.76 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C
8.33 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-1/-2
Melting Point 325 °C
617 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 150 °C
302 °F
long term; EMS
250 °C
482 °F
short term; EMS
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 215 °C
419 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
dry; IEC 60093
1.00e+13 ohm-cm
1.00e+13 ohm-cm
conditioned; IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Strength 30.0 kV/mm
762 kV/in
dry; IEC 60243-1
30.0 kV/mm
762 kV/in
conditioned; IEC 60243-1
Comparative Tracking Index 600 V
600 V
conditioned; IEC 60112
Descriptive Properties Value Comments
Automotive Exterior
Fuel systems
Interior
Powertrain and Chassis
Electricals & Electronics Electrical appliances
Energy distribution
Form Granules
Industry & Consumer goods Housewares
Hydraulics & Pneumatics
Mechanical Engineering
Power transmission
Sports & Leisure
Tools & Accessories
Processing Injection Molding
Special Characteristics Improved heat resistance
Improved UV resistance (outdoor use)