- PolyOne Lubri-Tech™ AT-10CF/15T-2S Acetal-Copolymer, Carbon Fiber Reinforced, PTFE/Silicone Lubricated (disco
PolyOne Lubri-Tech™ AT-10CF/15T-2S Acetal-Copolymer, Carbon Fiber Reinforced, PTFE/Silicone Lubricated (disco
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-10CF/15T-2S Acetal-Copolymer, Carbon Fiber Reinforced, PTFE/Silicone Lubricated
(disco.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE/Silicone LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Water Absorption | 0.18 % @Thickness 3.17 mm |
0.18 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 5.17 GPa | 750 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.507 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.950 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Molding |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG47 ABS
- Qualchem Danamid FES Polyamide 6
- Solvay Engineered Polymers SEQUEL® 1718HFLS Engineered Polyolefin (discontinued **)
- KB Alloys 20% Chromium Aluminum Alloy
- Industrial Laminates/Norplex NP634 Laminate
- Lubrizol Advanced Materials PEARLBOND® 125/H Linear Thermoplastic Polyurethane
- Total Lumicene® M 3410 EP HDPE Film, sheet
- DSM Akulon® K224-G6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry)
- A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy
- DuPont Performance Polymers AquaStik® AQS-2161 Polychloroprene Latex (discontinued **)
Copyright © lookpolymers.com All Rights Reserved