BASF Ultrason® E 2010 MR HP PESU

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer BASF
Trade Name Ultrason®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason® E 2010 MR HP PESU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced, medium viscosity standard injection molding grade for improved demolding behavior with Mold Release. PES-Blend with improved processibility. (High Productivity) Abbreviated designation according to ISO 1043-1: PESU.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.700 - 0.800 g/cc
0.0253 - 0.0289 lb/in³
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Water Absorption 1.7 %
1.7 %
ISO 62
Moisture Absorption at Equilibrium 0.50 %
0.50 %
23°C; 50% RH; ISO 62
Viscosity Measurement 56
56
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0076 cm/cm
0.0076 in/in
ISO 2577, 294-4
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
ISO 2577, 294-4
Melt Flow 93.1 g/10 min

@Load 10.0 kg,
Temperature 360 °C
93.1 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 192 MPa
27800 psi
ISO 2039-1
Tensile Strength, Yield 85.0 MPa
12300 psi
50mm/min; ISO 527-1/-2
Elongation at Break 80 %
80 %
Nominal; ISO 527-1/-2
Elongation at Yield 6.4 %
6.4 %
50mm/min; ISO 527-1/-2
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-1/-2
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 °C
428 °F
Decomposition Temperature >= 400 °C
>= 752 °F
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper throat
Zone 1 340 °C
644 °F
Feed zone
Zone 2 350 °C
662 °F
Compression
Zone 3 360 °C
680 °F
Metering-zone
Zone 4 360 °C
680 °F
Nozzle
Melt Temperature 360 °C
680 °F
Optimal
340 - 390 °C
644 - 734 °F
Injection molding/extrusion
Mold Temperature 140 - 180 °C
284 - 356 °F
Injection molding
160 °C
320 °F
Optimal
Drying Temperature 140 °C
284 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature 580-600°C
DIN 54836