- PolyOne Edgetek® RA-13CF/000 Polyarylsulfone, Carbon Fiber Reinforced (discontinued **)
PolyOne Edgetek® RA-13CF/000 Polyarylsulfone, Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyarylsulfone (PAS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® RA-13CF/000 Polyarylsulfone, Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 152 MPa | 22000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1000 ohm | 1000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 - 388 °C | 650 - 730 °F | Molding |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Kemex™ V96E
- Greene Tweed Xycomp® 1030-02 Carbon/Nylon 12 Composite
- Spartech Royalite R60M Hi-Impact ABS/PVC Resin
- Solvay ANTAROX® AG/5 Surfactant
- SABIC Innovative Plastics NORYL HN731A PPE+PS
- UBE 5034MT2 Nylon 6/66 Monofilament (Drawing Ratio=4.5)
- Polyplastics Duracon® ES-5 Acetal Co-polymer (POM), Conductive, Antistatic
- BASF Ultramid® B40 PA6
- Parker Chomerics CHO-FORM 5515 Conductive Silicone
- Fainplast Compounds PG 6620 Flexible PVC, Extrusion Modified with Rubber
Copyright © lookpolymers.com All Rights Reserved