Overview of materials for Polyaryletherketone (PAEK), Carbon Fiber Filled

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyaryletherketone (PAEK), Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.33 - 1.53 g/cc
0.0480 - 0.0553 lb/in³
Average value: 1.43 g/cc Grade Count:18
Filler Content 30.0 %
30.0 %
Average value: 30.0 % Grade Count:4
Water Absorption 0.0100 - 0.200 %
0.0100 - 0.200 %
Average value: 0.0969 % Grade Count:16
Viscosity 240000 - 790000 cP

@Temperature 400 - 400 °C
240000 - 790000 cP

@Temperature 752 - 752 °F
Average value: 485000 cP Grade Count:6
240000 - 790000 cP

@Shear Rate 1000 - 1000 1/s
240000 - 790000 cP

@Shear Rate 1000 - 1000 1/s
Average value: 485000 cP Grade Count:6
Linear Mold Shrinkage 0.000 - 0.00900 cm/cm
0.000 - 0.00900 in/in
Average value: 0.00184 cm/cm Grade Count:17
Linear Mold Shrinkage, Transverse 0.00400 - 0.0190 cm/cm
0.00400 - 0.0190 in/in
Average value: 0.0104 cm/cm Grade Count:14
Melt Flow 0.800 - 18.0 g/10 min
0.800 - 18.0 g/10 min
Average value: 4.15 g/10 min Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Rockwell M 82.0 - 108
82.0 - 108
Average value: 98.6 Grade Count:10
Hardness, Shore D 87.0 - 91.0
87.0 - 91.0
Average value: 89.7 Grade Count:3
Tensile Strength, Ultimate 95.0 - 262 MPa
13800 - 38000 psi
Average value: 177 MPa Grade Count:16
45.0 - 160 MPa

@Temperature -50.0 - 250 °C
6530 - 23200 psi

@Temperature -58.0 - 482 °F
Average value: 101 MPa Grade Count:1
Tensile Strength, Yield 95.0 - 821 MPa
13800 - 119000 psi
Average value: 286 MPa Grade Count:10
75.0 - 275 MPa

@Temperature -50.0 - 250 °C
10900 - 39900 psi

@Temperature -58.0 - 482 °F
Average value: 169 MPa Grade Count:1
Elongation at Break 0.800 - 25.0 %
0.800 - 25.0 %
Average value: 2.80 % Grade Count:15
Elongation at Yield 1.50 - 25.0 %
1.50 - 25.0 %
Average value: 5.21 % Grade Count:4
Modulus of Elasticity 2.96 - 55.8 GPa
430 - 8090 ksi
Average value: 21.3 GPa Grade Count:19
Flexural Yield Strength 186 - 894 MPa
27000 - 130000 psi
Average value: 311 MPa Grade Count:19
Flexural Modulus 4.20 - 51.4 GPa
609 - 7450 ksi
Average value: 18.7 GPa Grade Count:19
Compressive Yield Strength 107 - 574 MPa
15500 - 83200 psi
Average value: 220 MPa Grade Count:9
Shear Strength 51.7 - 98.0 MPa
7500 - 14200 psi
Average value: 80.1 MPa Grade Count:8
Izod Impact, Notched 0.350 - 0.800 J/cm
0.656 - 1.50 ft-lb/in
Average value: 0.575 J/cm Grade Count:15
Izod Impact, Unnotched 3.20 J/cm - NB
5.99 ft-lb/in - NB
Average value: 5.33 J/cm Grade Count:14
Izod Impact, Notched (ISO) 5.80 - 9.60 kJ/m²
2.76 - 4.57 ft-lb/in²
Average value: 7.75 kJ/m² Grade Count:6
Izod Impact, Unnotched (ISO) 25.0 - 39.0 kJ/m²
11.9 - 18.6 ft-lb/in²
Average value: 33.0 kJ/m² Grade Count:6
Charpy Impact Unnotched 2.50 - 3.00 J/cm²
11.9 - 14.3 ft-lb/in²
Average value: 2.70 J/cm² Grade Count:3
2.00 - 2.50 J/cm²

@Temperature -30.0 - -30.0 °C
9.52 - 11.9 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 2.25 J/cm² Grade Count:2
K (wear) Factor 10100 x 10-8 mm³/N-M
5000 x 10-10 in³-min/ft-lb-hr
Average value: 10100 x 10<sup>-8</sup> mm³/N-M Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 5.00 - 46.8 µm/m-°C
2.78 - 26.0 µin/in-°F
Average value: 11.6 µm/m-°C Grade Count:8
Specific Heat Capacity 1.17 - 1.81 J/g-°C

@Temperature 50.0 - 200 °C
0.280 - 0.433 BTU/lb-°F

@Temperature 122 - 392 °F
Average value: 1.51 J/g-°C Grade Count:6
Thermal Conductivity 0.0370 - 0.700 W/m-K
0.257 - 4.86 BTU-in/hr-ft²-°F
Average value: 0.378 W/m-K Grade Count:8
Melting Point 340 - 372 °C
644 - 702 °F
Average value: 349 °C Grade Count:11
Maximum Service Temperature, Air 220 - 260 °C
428 - 500 °F
Average value: 248 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi) 160 - 368 °C
320 - 694 °F
Average value: 287 °C Grade Count:17
Vicat Softening Point 280 - 320 °C
536 - 608 °F
Average value: 307 °C Grade Count:3
Glass Transition Temp, Tg 150 - 343 °C
302 - 649 °F
Average value: 171 °C Grade Count:11
Flammability, UL94 V-0
V-0
Grade Count:9
Electrical Properties Metric English Comments
Electrical Resistivity 20.0 - 1.00e+8 ohm-cm
20.0 - 1.00e+8 ohm-cm
Average value: 2.00e+7 ohm-cm Grade Count:5
Surface Resistance 10000 - 1.00e+6 ohm
10000 - 1.00e+6 ohm
Average value: 340000 ohm Grade Count:3
Insulation Resistance 100000 - 1.00e+6 ohm
100000 - 1.00e+6 ohm
Average value: 400000 ohm Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 390 - 425 °C
734 - 797 °F
Average value: 399 °C Grade Count:6
Nozzle Temperature 360 - 425 °C
680 - 797 °F
Average value: 393 °C Grade Count:13
Melt Temperature 354 - 420 °C
669 - 788 °F
Average value: 376 °C Grade Count:10
Mold Temperature 149 - 230 °C
300 - 446 °F
Average value: 183 °C Grade Count:13
Drying Temperature 120 - 150 °C
248 - 302 °F
Average value: 146 °C Grade Count:13