PolyOne Edgetek® PS-20CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PS-20CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.376 g/cc | 1.376 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0015 - 0.0020 cm/cm | 0.0015 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 124 MPa | 18000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 1000 ohm-cm | 10 - 1000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 277 °C | 470 - 530 °F | Molding |
| Mold Temperature | 82.2 - 110 °C | 180 - 230 °F | |
| Drying Temperature | 82.2 - 110 °C | 180 - 230 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CP - 86 General Purpose Acrylic Resin
- Quadrant EPP Ketron® 1000 IM Injection Molded Unfilled Polyetheretherketone (ASTM Product Data Sheet)
- SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Asia Pacific)
- Eastman Voridian E6838-010A Polyethylene (discontinued **)
- Gouda Vuurvast CURON 145 F Sp Dense Refractory Castable
- Kraton® D1117 P (SIS) Linear Block Copolymer
- Henkel Hysol PL 737 Film Adhesive
- SABIC Innovative Plastics LNP STAT-LOY SLDM2005 PC (Asia Pacific)
- Fainplast Compounds CL 63/K Flexible PVC, Sheathing
- BASF Novolen® 1100 RC Polypropylene, Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved