Asia International Enterprise (Hong Kong) 3010FW Polybutylene terephthalate
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Asia International Enterprise (Hong Kong) 3010FW Polybutylene terephthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc <br>@Temperature 23.0 °C |
1.30 g/cc <br>@Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 0.00 % | 0.00 % | |
| Linear Mold Shrinkage | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C |
30 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 60.8 MPa | 8820 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | 5mm/min; ASTM D638 |
| Flexural Strength | 99.0 MPa | 14400 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.78 GPa | 403 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm <br>@Thickness 3.17 mm,<br> Temperature 23.0 °C |
0.735 ft-lb/in <br>@Thickness 0.125 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | V-0 <br>@Thickness 1.50 mm |
V-0 <br>@Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Cylinder Temperature |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour |
Users viewing this material also viewed the following:
- Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized (discontinued **)
- Fainplast Compounds RI 54 Rigid PVC, Injection Molding
- Freudenberg Simrit E425 Hydrocarbon Elastomer
- H.C. Starck Amperit® 140.1 Tungsten (W)
- A. Schulman POLYBATCH™ CE-505-B Concentrate Based In Polyethylene
- DayGlo Gem-Tone GC-18F Emerald Green
- HP Alloys Alloy 718, 30% Cold Worked
- LG Chemical LG-512 Styrene-Butadiene-Styrene
Copyright © lookpolymers.com All Rights Reserved